Epoxy glue FFE-200. For leveling and final bonding of teak panels and boards/decks. Teackdecking Systems. 7,6L
FFE-200 Epoxy Adhesive is a high quality, lightweight, flexible, two component epoxy (resin and hardener) for teak decks.
Used for leveling and final bonding of teak panels and boards.
Easily sanded, no primer required.
Can be worked at temperatures up to 7°C.
Does not require a primer.
Cookie color.
Ratio of 1 : 1.
Consumption : from 0.8m² to 1.2m².
Also available in 1.5L
Consulter la description complète
FFE-200 epoxy glue is a high quality, lightweight, flexible two component epoxy (resin and hardener).
It is used for leveling and final bonding of teak panels and boards.
Easily sandable, it does not require any primer.
FFE-200 has a 1:1 ratio (one volume to one volume).
Once the two components are mixed, you can immediately apply the epoxy to your surface.
The adhesive has a density of 0.85kg when cured and its structure is a sound and thermal insulator.
Its viscosity is formulated to be high enough to stay in place when applied to the deck but low enough to provide excellent bonding strength.
Apply one coat at approximately 25°C ambient temperature with a 4.8 mm notched squeegee.
Open time 60-70 minutes, FFE-200 will cure in 4-6 hours and will be fully cured in 24 hours. Can cure up to 7°C.
Its advantages:
- Very good adhesion
- Medium viscosity for easy spreading and leveling
- Resistant to shocks and torsion
- Good curing even at low temperatures (up to 7°C)
- Mixing ratio, 1 volume to 1 volume
- Cookie color to match wood color
Classified as non-hazardous, no shipping label required.
Consumption: 7 to 10m²/KG
Cookie color. Available in 7.6 KG.
Sold in pocket format with their seals to facilitate the mixing.
Data sheet
- Brand
- TEAKDECKING SYSTEMS (TDS)
- Packaging
- 2 composants
- Consumption
- 7 à 10 m²/KG
- Composition A component
- bisphenol-A-epichlorhydrin epoxy resins (average molecular weight ≤ 700), bisphenol F epichlorhydrin spirit and co-Formaldehyde, Oxirane, mono [(C12-14 alcoholates) methyl derivatives]
- Composition B component
- Dimeras, oligomers, triethylenetetramine, C18-Unsat, dimers, polymers w / 3,3'-. [Oxybis (2,1-ethyleneoxy)] bis (1-propanamine), m-Xylene-α, α'-diamine, benzyl alcohol, 2,4,6-Tris (dimethylaminomethyl) phenol, triethylenetetramine
- Open time
- 60-70 minutes
- Polymerization time
- 4-6 hours
- Total polymerization time
- 24 hours