English GB- Hardeners : fast curing (224), medium curing (226), slow curing (229)
- Packaging : 0.286 kg, 1.43 kg, 7.16 kg, 64.35 kg and 286 kg
- Designed for epoxy laminating resins LAM-125 & 135 and the biobased version LAM125-G
- Material compatibility : wood, metal, all reinforcement fabrics, carbon and kevlar
- Wear, moisture and heat resistance
- High thermal performance
Consulter la description complète
LAM-224, LAM-226 and LAM-229 hardeners in combination with LAM-125, LAM-135 resins and the biobased LAM-125G version are designed for wet lay-up techniques. These systems enable the manufacture of lightweight, high-performance composite structures.
A variety of curing times are available to suit your projects : fast (224), medium (226) and slow (229) curing.
These systems adhere to base materials, wood, metal and all reinforcing fabrics.
They are resistant to moisture, heat and wear.
These epoxies develop excellent physical properties at room temperature and can be post-cured for optimum performance.
- Hardener packaging : available in 0.286kg, 1.43kg, 7.16kg, 64.35kg and 286kg
- Mixing ratio by volume : 3:1 (Resin:Hardener)
Resin and hardeners are sold separately.
- Available resin packaging : 1kg, 5kg, 25kg, 225kg and 1000kg
| Technical data LAM-125/LAM-224 | Technical data LAM-135/LAM-224 | |
| Shelf life in 150g pot: 11-15 minutes at 25°C | Shelf life in 150g pot: 11-15 minutes at 25°C | |
| Mixed viscosity: 544 cP à 25°C | Mixed viscosity: 1360 cP à 25°C | |
| Hardness Type D: 92 | Hardness Type D: 88 | |
| Compressive strength: 116 MPa | Compressive strength: 98 MPa | |
| Tensile strength: 56 MPa | Tensile strength: 77 MPa | |
| Flexural strength: 105 MPa | Flexural strength: 117 MPa | |
| Ultimate Tg: 88°C | Ultimate Tg: 101°C |
| Technical data LAM-125/LAM-226 | Technical data LAM-135/LAM-226 | |
| Shelf life in 150g pot: 56-70 minutes at 25°C | Shelf life in 150g pot: 44-54 minutes at 25°C | |
| Mixed viscosity: 616 cP à 25°C | Mixed viscosity: 1124 cP à 25°C | |
| Hardness Type D: 87 | Hardness Type D: 92 | |
| Compressive strength: 112 MPa | Compressive strength: 111 MPa | |
| Tensile strength: 79 MPa | Tensile strength: 66 MPa | |
| Flexural strength: 126 MPa | Flexural strength: 104 MPa | |
| Ultimate Tg: 89°C | Ultimate Tg: 98°C |
| Technical data LAM-125/LAM-229 | Technical data LAM-135/LAM-229 | |
| Shelf life in 150g pot: 98-120 minutes at 25°C | Shelf life in 150g pot: 80-97 minutes at 25°C | |
| Mixed viscosity: 525 cP à 25°C | Mixed viscosity: 1098 cP à 25°C | |
| Hardness Type D: 91 | Hardness Type D: 92 | |
| Compressive strength: 114 MPa | Compressive strength: 110 MPa | |
| Tensile strength: 61 MPa | Tensile strength: 61 MPa | |
| Flexural strength: 101 MPa | Flexural strength: 92 MPa | |
| Ultimate Tg: 86°C | Ultimate Tg: 94°C |
For further information, please consult the product data sheet.