Résine époxy Bio sourcée infusion Pro-set 5Kg
- INF-117G : bio-sourced infusion epoxy resin for an eco-responsible approach
- Very low viscosity, facilitates penetration and enhances adhesion
- Medium (2048) and slow (2049) curing hardeners
- Packaging : available in 5kg and 25kg
- Long-term resistance
Consulter la description complète
Designed for the manufacture of lightweight, high-performance composites, Pro-Set INF-117G biosourced epoxy infusion resin is a solution resistant to long-term cyclic loads and extreme conditions.
Thanks to its low viscosity, it guarantees exceptional impregnation and adhesion.
For even better performance, INF-117G can be post-cured.
- Resin packaging : available in 5kg and 25kg.
- Bio-sourced hardeners : medium cure (2048) and slow cure (2049)
- Hardener packaging : available in 1.7kg and 2x 4.25kg
Technical properties INF-117G / INF-2048 (Room temperature x 1 week)
- Mixing ratio by weight : 2.94:1 (Resin:Hardener)
- Mixing ratio by volume : 2.56:1 (Resin:Hardener)
- Hardness (Type D) : 83
- Mixed viscosity 25°C : 440 mPas
- Compressive strength : 94.1 MPa
- Tensile strength : 64.8 MPa
- Tensile elongation : 2.8
- Flexural strength : 99.5 MPa
- Ultimate Tg by DMA : 65°C
- Ultimate Tg by DSC : 69.6°C
Technical properties INF-117G / INF-2049 (Ambient temperature x 24H + 50°C x 16H)
- Mixing ratio by weight : 2.94:1 (Resin:Hardener)
- Mixing ratio by volume : 2.44:1 (Resin:Hardener)
- Hardness (Type D) : 82
- Mixed viscosity 25°C : 220 mPas
- Compressive strength : 86.8 MPa
- Tensile strength : 58.4 MPa
- Tensile elongation : 4.5
- Flexural strength : 96 MPa
(Gelling at TA + 50°C x 16H)
- Ultimate Tg by DMA : 65°C
- Ultimate Tg by DSC : 69.6°C
For further information, please consult the product data sheet.