Low Viscosity Epoxy Laminating Resin LAM-125 PRO-SET, 1kg
- LAM-125 : Low-viscosity epoxy laminating resin & LAM-135 : Medium-viscosity epoxy laminating resin
- Packaging : 1kg, 5kg, 25kg, 225kg and 1000kg
- Available hardeners : fast (210), medium (211), slow (211), super-slow (213) curing
- Ability to adhere to a wide range of materials (wood, metal, etc.)
- Excellent moisture resistance,
- Superior resistance to heat and wear
- For an ecological alternative, discover our biosourced epoxy laminating resin : LAM-125G
Consulter la description complète
PRO-SET® low-viscosity LAM-125 epoxy resin & medium-viscosity LAM-135 epoxy resin are versatile systems designed for a wide range of wet lamination applications.
PRO-SET laminating resins are used to produce lightweight, high-performance composite structures that withstand long-term cyclic loading in the most demanding environments.
These epoxies develop excellent physical properties at room temperature and can be post-cured for enhanced performance.
These resins have the ability to adhere to many types of material, including wood, metal and all reinforcing fabrics.
- Excellent moisture resistance
- Superior heat resistance
- Superior wear resistance
- Resin packaging : 1kg, 5kg, 25kg, 225kg and 1000kg
Resin and hardeners sold separately.
- Hardeners available : fast curing (224), medium curing (226), slow curing (229)
- Hardener packaging : available in 0.286kg, 1.43kg, 7.16kg, 64.35kg and 286kg
- Mixing ratio by volume : 3:1 (Resin:Hardener)
To complement these systems, discover an environmentally-friendly alternative with our biosourced epoxy laminating resin: LAM-135G.
Technical properties LAM-125
- Low viscosity : designed for rapid wetting of composite fabrics, especially Kevlar and carbon fiber.
- Mixed viscosity 25°C : 449-616 MPas
- Compressive strength : 96 MPa
- Tensile strength : 70 MPa
- Tensile elongation : 5.6
- Flexural strength : 124 MPa
- Ultimate Tg by DMA : > 89 °C
- Ultimate Tg by DSC : > 89.5 °C
Technical properties LAM-135
- Medium viscosity : designed for manual wetting, vacuum bagging, filament winding and machine impregnation. Ideal for specific operations such as taping and tabbing in the assembly of composite structures.
- Mixed viscosity 25°C : 904-1360 MPas
- Compressive strength : 101 MPa
- Tensile strength : 74 MPa
- Tensile elongation : 6.2
- Flexural strength : 128 MPa
- Ultimate Tg by DMA : > 102 °C
- Ultimate Tg by DSC : > 102.5 °C
For further information, please consult the product data sheet.