ENTROPY 305 biobased resin. For high temperature compression molding processes
Biobased epoxy resin for compression molding processes for fast cycling
Rapid heat activated polymerization for high temperature compression molding processes.
Common uses: Skis and Snowboards, Skateboards, Compression molding composites, Wood laminates.
Super Sap® formulation.
28% biobased content
USDA BioPreferred® certified
Consulter la description complète
305 resin is a compression moulding resin for fast cycle times in heat assisted moulding processes of fibre reinforced composites.
The 305 system has a high biological content, excellent fibre impregnation qualities and thixotropic characteristics to limit sag in high temperature curing applications.
High modulus combined with excellent elongation properties results in durable but lightweight composite parts.
Epoxy resin 305 is a USDA BioPreferred product with a 28% biobase content.
Usage: skateboard, skis, snowboards, press moulded composites
Consumption: approx. 3 litres for 2 snowboards or 2 pairs of skis
Tip for use :
- For best results, mix the two components according to the weight.
- Always stir the product thoroughly for at least 2 minutes, scraping all surfaces of the container to ensure a homogeneous mixture.
- Use the product in an environment with cold ambient temperatures or high humidity.
- For optimum curing performance, ensure that the surfaces are dry and free of all dirt, debris and/or traces of oil. Surface preparation by sanding is strongly recommended.
- Carry out preliminary tests with the materials and processes being considered to fully understand the curing characteristics of epoxy in your materials working environment.
Available options :
305 CPM resin + CPF fast hardener
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:40
Mixing viscosity (cPs) at 25°C: 1994
Time of use at 25°C: 20 minutes
Recommended complete curing time: 15 minutes at 82°C
Characteristics: superior adhesion, very low viscosity to facilitate fibre wetting and accelerate polymerisation for high speeds.
305 CPM resin + CPS fast hardener
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:38
Mixing viscosity (cPs) at 25°C: 1546
Time of use at 25°C: 50 minutes
Recommended complete curing time: 20 minutes at 82°C
Characteristics: superior adhesion, very low viscosity to facilitate fibre wetting.