Two-component epoxy glue light, flexible and easy to sand. Can be working up to 7 ° C.
Does not require any primer. Biscuit color. Available in 7.6 KG.
Sold in pocket format with their seal to facilitate mixing. Ratio of 1: 1.
FFE-200 Fairing & Bonding Epoxy is a custom blended flexible mastic of high-quality epoxy resins and activators, and engineered fillers to yield a light weight, flexible and easily-sanded system used for both fairing of deck substrates and the final glue-down of deck panels. FFE-200 weighs only 8 lb (3.6 kg) per gallon container when cured and its cell-like structure makes it an excellent sound and thermal insulator. The viscosity of the FFE-200 is formulated to be high enough to stay in place when used for fairing, but low enough to provide excellent wet-out for bonding. The FFE-200 Fitting & Fairing Epoxy will cure in temperatures as low as 45°F (7°C).
Developed to be user-friendly, the simplified 1:1 mix ratio allows a batch of any size to be easily measured and mixed. Once thoroughly mixed, the material can be spread immediately, requiring no induction time. At 77°F (25°C), a layer of FFE-200 applied with a 3/16" (4.8mm) toothed trowel will have an open time of approximately 60-70 minutes, the material will set in approximately 4-6 hours, and complete cure will be achieved in approximately 24 hours. This bonding epoxy has US Department of Transportation “non-corrosive” classification so it does not require hazardous labeling for shipment.
COVERAGE: 7 to 10 m² /KG
|2||2%||Up to 2,51 €|
|3||4%||Up to 7,53 €|
|4||6%||Up to 15,06 €|
|5||8%||Up to 25,10 €|
|Brand||TEAKDECKING SYSTEMS (TDS)|
|Consumption||1 à 1.5m²/KG|
|Composition A component||bisphenol-A-epichlorhydrin epoxy resins (average molecular weight ≤ 700), bisphenol F epichlorhydrin spirit and co-Formaldehyde, Oxirane, mono [(C12-14 alcoholates) methyl derivatives]|
|Composition B component||Dimeras, oligomers, triethylenetetramine, C18-Unsat, dimers, polymers w / 3,3'-. [Oxybis (2,1-ethyleneoxy)] bis (1-propanamine), m-Xylene-α, α'-diamine, benzyl alcohol, 2,4,6-Tris (dimethylaminomethyl) phenol, triethylenetetramine|
|Open time||60-70 minutes|
|Polymerization time||4-6 hours|
|Total polymerization time||24 hours|