Epoxy adhesive FFE-200 7.6kg

321,77 € Tax included

Two-component epoxy glue light, flexible and easy to sand. Can be working up to 7 ° C.

Does not require any primer. Biscuit color. Available in 7.6 KG.

Sold in pocket format with their seal to facilitate mixing. Ratio of 1: 1.

FFE-200 Fairing & Bonding Epoxy is a custom blended flexible mastic of high-quality epoxy resins and activators, and engineered fillers to yield a light weight, flexible and easily-sanded system used for both fairing of deck substrates and the final glue-down of deck panels. FFE-200 weighs only 8 lb (3.6 kg) per gallon container when cured and its cell-like structure makes it an excellent sound and thermal insulator. The viscosity of the FFE-200 is formulated to be high enough to stay in place when used for fairing, but low enough to provide excellent wet-out for bonding. The FFE-200 Fitting & Fairing Epoxy will cure in temperatures as low as 45°F (7°C).

Developed to be user-friendly, the simplified 1:1 mix ratio allows a batch of any size to be easily measured and mixed. Once thoroughly mixed, the material can be spread immediately, requiring no induction time. At 77°F (25°C), a layer of FFE-200 applied with a 3/16" (4.8mm) toothed trowel will have an open time of approximately 60-70 minutes, the material will set in approximately 4-6 hours, and complete cure will be achieved in approximately 24 hours. This bonding epoxy has US Department of Transportation “non-corrosive” classification so it does not require hazardous labeling for shipment.

COVERAGE: 7 to 10 m² /KG

Quantity Discount You Save
2 2% Up to 12,87 €
3 4% Up to 38,61 €
4 6% Up to 77,22 €
5 8% Up to 128,71 €
Packaging 2 composants
Consumption 7 à 10 m²/KG
Composition A component bisphenol-A-epichlorhydrin epoxy resins (average molecular weight ≤ 700), bisphenol F epichlorhydrin spirit and co-Formaldehyde, Oxirane, mono [(C12-14 alcoholates) methyl derivatives]
Composition B component Dimeras, oligomers, triethylenetetramine, C18-Unsat, dimers, polymers w / 3,3'-. [Oxybis (2,1-ethyleneoxy)] bis (1-propanamine), m-Xylene-α, α'-diamine, benzyl alcohol, 2,4,6-Tris (dimethylaminomethyl) phenol, triethylenetetramine
Open time 60-70 minutes
Polymerization time 4-6 hours
Total polymerization time 24 hours