CCR is a low-viscosity, water-clear, UV-resistant epoxy resin designed specifically for casting and moulding applications.
Its low viscosity allows bubble-free and crystalline casting, ideal for artistic and leisure applications.
The system features two cure rates: slow (CCS) for high density casting resin applications and fast (CCF) for fast casting resin applications for small projects, such as resin jewellery and others.
CCS is a USDA BioPreferred certified product with a 30% biobase content.
Use: jewellery, thick coatings, castings
Density: fast: 250g/231ml for a maximum thickness of 62mm / slow: 1000g/935ml for a maximum thickness of 100mm
Working temperature: between 15°C and 25°C
Tip for use :
Tensile modulus (ASTM D638): 3.0 GPa
Tensile strength (ASTM D638): 54.5 MPa
Elongation (ASTM D638): 6.5%.
Flexural modulus (ASTM D790) : 2.8 GPa
Flexural strength (ASTM D790): 76.5 MPa
Compressive strength (ASTM D695): 74.9 MPa
Ultimate Tg: 52°C
Hardness (shore D): 70-80
Mixing ratio (by volume): 2:1
Mixing ratio (by weight): 100:42
Viscosity (A/B/Mixed at 25°C): 2160/15/270 mPas
Component density (density at 25°C): 1.12 (resin), 0.95 (hardener) gcm-3
Mixture density (density at 25°C): 1.07 gcm-3
Time of use (at 25°C): 360 minutes
Dry to the touch (at 35°C): 72 hours
Recommended complete curing: 7 days at 25°C
VOC content (ASTM D2369): 8.0 g/l
Biosourced carbon content (ASTM D6866): 20%.
Characteristics: high transparency and low polymerisation speed, allowing the production of high thicknesses or large castings.
*Attention to humidity and the presence of water. The resin may become opaque. If this is the case, a heat gun must be used.