CCR is a low viscosity, water clear, UV resistant system designed specifically for casting and moulding applications.
Its low viscosity allows bubble-free and crystalline casting, ideal for artistic and leisure applications.
The system features two cure rates: slow (CCS) for high density casting resin applications and fast (CCF) for fast casting resin applications for small projects, such as resin jewellery and others.
CCS is a USDA BioPreferred certified product with a 30% biobase content.
Use: jewellery, thick coatings, castings
Consumption: fast: 250g/231ml for a cube of about 62mm / slow: 1000g/935ml for a cube of about 100mm
Working temperature: between 15°C and 25°C
Tip for use :
Tensile modulus (ASTM D638): 3.1 GPa
Tensile strength (ASTM D638): 56.1 MPa
Elongation (ASTM D638): 6%.
Flexural Modulus (ASTM D790): 2.7 GPa
Flexural strength (ASTM D790): 81.7 MPa
Compressive strength (ASTM D695): 85.4 MPa
Ultimate Tg: 51°C
Hardness (shore D): 70-80
Mixing ratio (by volume): 2:1
Mixing ratio (by weight): 100:43
Viscosity (A/B/Mixed at 25°C): 2160/30/370 mPas
Component density (density at 25°C): 1.12 (resin), 0.97 (hardener) gcm-3
Density of the mixture (density at 25°C): 1.08 gcm-3
Time of use (at 25°C): 90 minutes
Dry to the touch (at 35°C): 24 hours
Recommended complete curing: 7 days at 25°C
VOC content (ASTM D2369): 9.2 g/l
Biosourced carbon content (ASTM D6866): 20%.
Characteristics: high transparency and low polymerisation speed, allowing the production of high thicknesses or large castings.
*Attention to humidity and the presence of water. The resin may become opaque. If this is the case, a heat gun must be used.
|Packaging||Kit of 7.10kg|